大尺寸Br晶体生长和性能研究摘要：KBr(Potassium bromide)为关键的离子化合物，是无色结晶或白色粉末，有强烈咸味，见光色变黄。KBr吸湿性，水溶液呈中性，主用途是光谱分析、点滴分析测定铜及银、极谱分析铟镉和砷。在感光材料工业作为制造感光胶片、显影药、底片加厚剂、调色剂和彩色照片漂白剂等。医药上做神经镇静剂（三溴片）。此外还作为化学分析试剂，分光和红外线的传递，制特种肥皂，以及雕刻、石印等方面。本文选择提拉法生长出优质大尺寸KBr晶体：对Br原料进行了纯化处理，选择提拉法生长Br品体，获得了合适的品体生长工艺参数：熔液上方温度梯度-20℃/cm`-30℃/cm,下方温度梯度10℃/cm15℃/cm,拉速14m/h,转速5~2Or/min。检测了KBr品体的红外光谱，表明纯化后的多品料能够有效去除杂质，有利于获得高透过、低吸收的品体。TG-DSC表明KBr在720.9℃发生熔化。XRD表明KBr品体属于立方品系，Fm3m空间群。测试了KB品体透过光谱，透过率大于92%。与此同时探索了KBr晶体生长的工艺条件。并对它的性能进行分析研究关键词：晶体生长提拉法工艺条件B肛性能Abstract:potassium bromide (Potassium bromide)is a typical ionic compound,is a colorless or white powder,has a strong color of yellow salty,see.Potassium bromide is hygroscopic and water solution is neutral.It ismainly used for spectroscopic analysis,spot analysis,determination of copper and silver,polarographic analysis of indium,cadmium and arsenic.In the photographic material industry,it is used in the manufacture of photographic films,photographic agents,negatives,thickening agents,toners,and color photo bleaching agents.Used medicinally as a nerve depressant(Tribromid Tablets).They are also used in chemical analysis reagents,forthe transmission of light and infrared,for special soap,and for engraving and lithography.In this paper,the growth of large size and high quality potassium bromide crystals by the Czochralski method of KBr raw materials were purified with KBr crystal grown by the Czochralski method,obtained the appropriate crystal growth parameters:melt temperature gradient above -20 DEG /cm-30 DEG /cm,the temperature gradient below 10 DEG /cm 15 DEG /cm,speed 14mm/h,rotation speed 5 20r/min.The infrared spectrum ofKBr crystal has been measured.The result shows that the purified polycrystalline material can effectively remove impurities and is beneficial to obtain high transmittance and low absorption crystal.TG-DSC shows that KBrmelts at 720.9.XRD shows that KBr crystal belongs to cubic system and Fm3m space group.The transmission spectrum of KBr crystal has been tested,and the transmittance is greater than 92%.At the same time,the technological conditions of KBr crystal growth were explored.And its performance isanalyzed and studiedKeywords:crystal growth,Czochralski method,technological conditions,KBr properties目录Abstract.................221.1KBr单晶体的发展和定义21.2国内外研究现状.......第2章KBr单晶体的制备和生长分析5552.1.2工艺方法和实验过程52.2晶体生长2.3实验中遇到的问题和解决方案6552.3.3晶体拉脱.....53.1晶体XYD分析.....83.3晶体红外透射分析8第四章KBr制备测试分析与讨论994.1.2原料选择和工艺概况104.1.3提拉法对比分析.…109994.3我国KBr发展分析和生长建议第五章结论…1212第一章绪论KBr晶体是一种具有良好性能的光学材料。经高能粒子束轰击、高能射线辐照或强激光照射后，皆可使之着色。由于着色KBr晶体具有独特光谱和激光特性而使之成为一种较有发展前途的光电子材料，现已被应作为非线性光学、宽可调谐色心激光和高密度光存储等方面。随着现代晶体制备、检测和实验等技术的进步，色心晶体研究和应用也有了进一步发展。特别是在光电子器件方面有较大潜在的应用前景，使得对色心晶体研究和应用等出现升温趋势。KBr晶体是具有高透过、低吸收和光学均匀性高的典型碱金属卤化物。随着科学技术的发展，国内外对红外光谱仪需求越来越广泛，则对优质大尺寸KBr窗片需要也逐渐上升。Br晶体1.1Br单晶体的发展和定义我国晶体生长有着悠久的历史，早在春秋战国甚至更早的时期，就有煮海为盐、炼制丹药等晶体生长的时间活动，而同时，世界上随着炼金术的兴起与发展，人工晶体生长，特别是人工晶体气相生长在全世界都有发现。进入二十世纪后，人工晶体生长才有飞跃式的发展，不仅体现在人工晶体生长理论、人工晶体生长技术上，而且，发现了一大批极有价值的新晶体，为科学进步和人类生活水平提高做出了巨大贡献。人工晶体生长的水平主要表现在技艺和科学两个方面，其中，晶体生长技术在晶体的研